搪瓷管经过高温焙烧、冷却后,搪瓷与钢板就粘结在了一起。由于搪瓷的线膨胀系数和延伸率小于钢板的特性,冷却后搪玻璃的变形量会小于钢板的变形量,而搪瓷受到钢板的约束就会产生压应力。也就是说搪瓷管制成后,搪玻璃会存在一种预压缩应力,而钢板则存在预拉伸应力。
Enamel tube through the high temperature roasting, cooling, enamel and steel te is bonded together. Because the characteristics of enamel of the coefficient of linear expansion and extension rate is less than the te, deformation after cooling glass lining will be less than the amount of deformation of steel, and steel te enamel ctrained will generate compressive stress. That is to say the enamel tube, glass lined there will be a pre compressive stress, and the steel te are pre tensile stress.
由于预应力与线膨胀系数和延伸率相关,搪瓷管空气预热器图片,而线膨胀系数、延伸率又与温度密切相关,因此搪瓷管的工作温度对瓷管本身的使用会带来很大的影响。在这里需要注意温度的变化,如果温度变化大,很容易使搪瓷产生的应力超过使用应力,从而引起搪瓷的破坏,一旦搪瓷层遇到冷、热急变,极易发生爆瓷现象。
Due to prestressing force and the coefficient of linear expansion and extension rate, and the coefficient of linear expansion,搪瓷管空气预热器采购, elongation and closely related with the temperature, so the enamel pipe working temperature on the porcelain tube itself use will have a great impact. Here we need to pay attention to the change of temperature, if the temperature change is big, easy to cause the enamel of stress over the use of stress, so as to cause enamel damage, once the enamel layer encountered cold and hot blast, prone to burst phenomenon of porcelain.
空气预热器两列下料温差大的原因
空气预热器两列下料温差过大一般有以下原因:
1、分料阀分料不均匀,A、B两列进料不均导致热耗不均匀从而温度不同;
2、A、B系列的窑尾喷煤管喷煤不均匀,窑尾喂煤称管道如果有两路分料阀,更容易出现此现象,分料的不均匀导致磨损不均匀,时间越长两路给煤量就差别越大。所以应及时检查两路分料阀的磨损情况和分料情况;
3、窑尾喷煤管的位置、角度不同也会产生温度差别;
4、窑尾喷煤管设备原因,搪瓷管空气预热器多少钱,检查是否部分堵塞或者磨通窜料等;
5、A、B是否有严重的漏风点,特别是热电偶附近的对温度影响更大。
搪瓷修补剂类似于一种工艺
提到了搪瓷,就不免的让人想到了瓷碗,因为这两个物品都是一种外边看着可坚硬,但实则却很脆弱的物品。记得以前曾经有一门可以将破了的碗进行修复的一个工艺,好像是叫做“锔碗”,这个锔碗就是一种对瓷碗修复的工艺,虽然现在的人们已经不再这样了,搪瓷管空气预热器,但是却也在历留下了我们追忆不回来的一页。那么对于瓷碗可以使用这种古老的工艺完成修复的工作,那么这个搪瓷呢?其实,搪瓷设备也是可以进行修复工作的,而且相比较于锔碗这种工艺来说,还更加的简单了,那就是用搪瓷修补剂来对搪瓷进行必要的修复工作,并且还很是简单和快捷哦。